Sisanra deede | Ijinna ti aaye eyikeyi lori dada oke ti veneer ti o yapa kuro ninu alaṣẹ iwuwo iwuwo taara | |
Ipari veneer 500 | Ipari veneer 1000 | |
≤15 | 2.0 | 4.0 |
15...≤25 | 1.5 | 3.0 |
25...≤60 | 1.0 | 2.0 |
> 60 | 1.0 | 1.5 |
Didara ifarahan
Nkan | Ibiti a gba laaye |
Ewiwu | Ko si aaye |
Gbigbọn | |
Òkú sorapo | |
Ajeji-ara Adhering | |
Iho kokoro | |
Rot | |
Kokoro | |
Igbẹgbẹ | Diẹ laaye, kii ṣe ipa ni lilo |
Ifarahan | |
Awọ-aidọgba ati asesejade | |
Awọn abulẹ fun sq.m lori dada | ≤3 |
Nkan Idanwo GB- Ṣaaju ifijiṣẹ Ayẹwo Factory
Nkan Idanwo | Ẹyọ | Standard | Ọna Idanwo | |
Inaro atunse Agbara | Si ọna A | Mpa | ≥65 | GB / T2634-2008 Igbeyewo Standard |
Si ọna B | ≥65 | |||
Inaro atunse modulus ti elasticity | Si ọna A | Gpa | ≥8 | |
Si ọna B | ≥8 | |||
Ibaramu (labẹ 20MPa) | Si ọna C | % | ≤3 | |
Crev | ≥70 | |||
Agbara ipa (idanwo ẹgbẹ) | Si ọna A | KJ/㎡ | ≥13 | |
Si ọna B | ≥13 | |||
Interlaminar rirun agbara | Mpa | ≥8 | ||
Agbara ina inaro (90 ℃ + 2 ℃) | KV/mm | ≥11 | ||
Agbara ina inaro (90 ℃ + 2 ℃) | KV | ≥50 | ||
iwuwo išẹ | g/cm³ | > 1.1 ~ 1.2 | ||
omi akoonu | % | ≤6 | ||
Isunku lẹhin gbigbe | Si ọna A | % | ≤0.3 | |
Si ọna B | ≤0.3 | |||
Si ọna sisanra | ≤3 | |||
Gbigba epo | % | ≥8 |